Darstellung von Co2-xZnxMo3O 8-Einkristallen mit definierter Zusammensetzung durch Chemischen Transport

Research output: Contribution to journal › Research article › Contributed › peer-review

Contributors

  • Udo Steiner - , TUD Dresden University of Technology (Author)
  • Werner Reichelt - , TUD Dresden University of Technology (Author)
  • Sofia Daminova - , Tomsk State University, TUD Dresden University of Technology (Author)
  • Enrico Langer - , Chair of Microstructure Physics (Author)

Abstract

Phase-pure powder samples of Co2-xZnxMo 3O8 mixed crystals were prepared by solid state reactions in evacuated quartz tubes at 1273 K. The lattice parameter were refined from X-ray powder pattern by the Rietveld method. A small but significant change of the lattice parameter of Co2-xZnxMo3O 8 as a function of the zinc content was observed, thus confirming the existence of a complete solid solution series. Single crystals of Co 2-xZnxMo3O8 were grown by means of chemical vapour transport in a temperature gradient 1273 K to 1173 K using NH4Cl or NH4Br as transport agent starting from a source material with a small oxygen excess, corresponding to a formal composition "Co2-xZnxMo3O8.1". The Co/Zn ratio of the obtained Co2-xZnxMo3O 8 single crystals was investigated using EDX measurements.

Translated title of the contribution
Preparation of Co2-xZnxMo3O8 mixed crystals with defined composition by chemical vapour transport

Details

Original languageGerman
Pages (from-to)364-368
Number of pages5
JournalZeitschrift fur Anorganische und Allgemeine Chemie
Volume631
Issue number2-3
Publication statusPublished - 2005
Peer-reviewedYes

Keywords

ASJC Scopus subject areas

Keywords

  • Chemical Vapor Transport, Mixed Crystals, Molybdenum