Functionalization of Ti64 via Direct Laser Interference Patterning and Its Influence on Wettability and Oxygen Bubble Nucleation

Research output: Contribution to journalResearch articleContributedpeer-review

Contributors

Abstract

The nucleation of bubbles on solid surfaces is an important phenomenon in nature and technological processes like electrolysis. During proton-exchange membrane electrolysis, the nucleation and separation of the electrically nonconductive oxygen in the anodic cycle plays a crucial role to minimize the overpotential it causes in the system. This increases the efficiency of the process, making renewable energy sources and the “power-to-gas” strategy more viable. A promising approach is to optimize gas separation by surface functionalization in order to apply a more advantageous interface to industrial materials. In this work, the connection between the wettability and bubble nucleation of oxygen is investigated. For tailoring the wettability of Ti64 substrates, the direct laser interference patterning method is applied. A laser source with a wavelength of 1064 nm and a pulse duration of 12 ps is used to generate periodic pillar-like structures with different depths up to ∼5 μm. The resulting surface properties are characterized by water contact angle measurement, scanning electron microscopy, confocal microscopy, and X-ray photon spectroscopy. It was possible to generate structures with a water contact angle ranging from 20° up to nearly superhydrophobic conditions. The different wettabilities are validated based on X-ray photon spectroscopy and the different elemental composition of the samples. The results indicate that the surface character of the substrate adapts depending on the surrounding media and needs more time to reach a steady state for deeper structures. A custom setup is used to expose the functionalized surfaces to oxygen-oversaturated solutions. It is shown that a higher hydrophobicity of the structured surface yields a stronger interaction with the dissolved gas. This significantly enhances the oxygen nucleation up to nearly 350% by generating approximately 20 times more nucleation spots, but also smaller bubble sizes and a reduced detachment rate.

Details

Original languageEnglish
Pages (from-to)2918-2929
Number of pages12
JournalLangmuir
Volume40
Issue number6
Early online date31 Jan 2024
Publication statusPublished - 13 Feb 2024
Peer-reviewedYes

External IDs

PubMed 38295345
Scopus 85184796058

Keywords

Sustainable Development Goals

Keywords

  • Water electrolysis, Surface-structures, Titanium, Evolution, Energy, Performance, Ti-6al-4v