Hochdämpfende Metall-Graphit-Verbundwerkstoffe in Werkzeugmaschinen Experimentelle Charakterisierung der Dämpfungswirkung von Metall-Graphit-Verbundwerkstoffen als Fugenbeilage in einer Vorschubachse
Publikation: Beitrag in Fachzeitschrift › Forschungsartikel › Beigetragen › Begutachtung
Beitragende
Abstract
In this article, iron graphite composite (EGr) with varying graphite content (from 20 to 80 %) and steel samples were manufactured using powder metallurgical method and characterized by resonance damping analysis. The EGr samples and steel samples as reference were used as spacer in a feed axis with a linear guide and the damping behavior was investigated using FFT and SFTF. The material damping of EGr increases with increased graphite content and EGr with 20 % shows the best damping capacity as it used in the feed axis.
Details
| Originalsprache | Deutsch |
|---|---|
| Seiten (von - bis) | 244-248 |
| Seitenumfang | 5 |
| Fachzeitschrift | ZWF Zeitschrift fuer Wirtschaftlichen Fabrikbetrieb |
| Jahrgang | 118 |
| Ausgabenummer | 4 |
| Publikationsstatus | Veröffentlicht - Apr. 2023 |
| Peer-Review-Status | Ja |
Externe IDs
| unpaywall | 10.1515/zwf-2023-1021 |
|---|---|
| Mendeley | 2e66d073-5ce1-3173-a26b-79f09b962fb2 |
| ORCID | /0000-0002-1093-2149/work/150883638 |
| ORCID | /0000-0002-9661-2540/work/156338125 |
Schlagworte
Forschungsprofillinien der TU Dresden
DFG-Fachsystematik nach Fachkollegium
Fächergruppen, Lehr- und Forschungsbereiche, Fachgebiete nach Destatis
Ziele für nachhaltige Entwicklung
ASJC Scopus Sachgebiete
Schlagwörter
- Dämpfung, Eisen-Graphit-Verbundwerkstoff, Linearführung, Pulvermetallurgie, Vorschubachse, Dämpfung, Eisen-Graphit-Verbundwerkstoff, Linearführung, Pulvermetallurgie, Vorschubachse