Foam-derived multiferroic BiFeO3 nanoparticles and integration into transparent polymer nanocomposites

Publikation: Beitrag in FachzeitschriftForschungsartikelBeigetragenBegutachtung

Beitragende

Abstract

Transparent BiFeO3/PMMA (PMMA = poly(methyl methacrylate)) nanocomposites with a thickness up to 40 μm are obtained via solution film casting of BiFeO3 nanoparticle dispersions. The multiferroic BiFeO3 nanoparticles are obtained in a space confined crystallisation process in a porous carbon matrix and subsequent removal of the matrix. The average crystallite size ranges from 46 nm to 106 nm for materials synthesised at 803 K and 903 K respectively, but, at higher temperature, significant amounts of side products are detected by means of X-ray powder diffraction. The nanoparticles are multiferroic with a magnetic coercivity of 1.88 A m-1 at 400 K and a polarisation of up to 1.04 μC/cm2 at 65 kV/cm (298 K). Surface functionalisation using oleic acid allows the integration into PMMA films with a high transmittance.

Details

OriginalspracheEnglisch
Seiten (von - bis)1-15
Seitenumfang15
Fachzeitschrift Journal of experimental nanoscience
Jahrgang3
Ausgabenummer1
PublikationsstatusVeröffentlicht - 16 Mai 2008
Peer-Review-StatusJa

Schlagworte

Schlagwörter

  • BiFeO, Multiferroic, Nanocomposite, Nanoparticles