A new titanium precursor, [Ti(OPrⁱ)₂(deacam)₂] (deacam = N,N-diethylacetoacetamide), was developed by the reaction of the parent Ti alkoxide with the β-ketoamide. The compound, obtained as a monomeric six-coordinated complex, was used in metal organic chemical vapor deposition (MOCVD) of TiO₂ both as a single source precursor (SSP) and in the presence of oxygen. The high thermal stability of [Ti(OPrⁱ)₂(deacam)₂] enabled the fabrication of TiO₂ films over a wide temperature range, with steady growth rates between 500 and 800 °C. The microstructure of the obtained systems was analyzed by X-ray diffraction (XRD) and Raman spectroscopy, whereas atomic force microscopy (AFM) and field emission-scanning electron microscopy (FE-SEM) measurements were performed to investigate the surface morphology and nanoorganization. Film composition was investigated by complementary techniques like Rutherford backscattering spectrometry (RBS), nuclear reaction analysis (NRA), X-ray photoelectron spectroscopy (XPS), and secondary ion mass spectrometry (SIMS). The electrical properties of the layers were investigated by performing capacitance voltage (C-V) and leakage current measurements.