Hollow Ni/C microsphere@graphene foam with dual-spatial and porous structure on the microwave absorbing performance
Publikation: Beitrag in Fachzeitschrift › Forschungsartikel › Beigetragen › Begutachtung
Beitragende
Abstract
In this study, a unique dual-spatial three-dimensional (3D) porous structure comprising Ni/C hollow microspheres was prepared from a Ni-based metal organic framework (Ni-MOF) embedded in graphene foam (GF) by the solvothermal method followed by calcination. The graphene foam-based composite, Ni/C@GF (NCGF), exhibited a stable spatial conductive network structure and diverse porous architecture, promoting the microwave absorption (MA) properties of composites. The NCGF with a Ni/C and GF ratio of 1:2.5 displayed a reflection loss (RL) value of ─63 dB with 15 wt% loading, while the thickness is only 1.76 mm. Further, its effective absorption bandwidth (EAB) reached to 5.4 GHz at 2 mm thickness. In addition, when the RL value is less than ─20 dB, the NCGF still manifests a wider bandwidth (2.2 GHz) and a relatively low thickness (1.76 mm). In addition to the extraordinary attenuation ability, the excellent MA performance is mainly ascribed to optimized impedance matching characteristics. Moreover, multiple reflections promoted by the dual-space structure also play a significant role during the microwave absorption process.
Details
Originalsprache | Englisch |
---|---|
Aufsatznummer | 159811 |
Fachzeitschrift | Journal of alloys and compounds |
Jahrgang | 873 |
Publikationsstatus | Veröffentlicht - 25 Aug. 2021 |
Peer-Review-Status | Ja |
Externe IDs
ORCID | /0000-0002-0666-3273/work/141545136 |
---|
Schlagworte
ASJC Scopus Sachgebiete
Schlagwörter
- Dual-spatial structure, Impedance matching, Microwave absorption, Multiple reflections