Highly transparent Bi2MoO6- and Bi2WO 6-polymer nanocomposites

Publikation: Beitrag in FachzeitschriftForschungsartikelBeigetragenBegutachtung

Beitragende

Abstract

A combined method of precipitation, phase transfer into organic solvent, solvothermal treatment and subsequent in situ polymerization was used to integrate nanocrystalline Bi2MoO6- and Bi 2WO6- particles into a polymer matrix of poly-laurylacrylate. The presented method offers a new and gentle way to produce highly transparent bulk nanocomposites containing evenly distributed Bi 2MoO6- and Bi2WO6-nanoparticles. Characterization results of DLS-, XRD-, REM- and TEM-measurements are presented as well as solid state UV/VIS-measurements of the particles. The transparent nanocomposites were characterized using UV/VIS-spectroscopy and ellipsometry. All composites show a good transmission in the range from 800-400 nm. The particle content of the nanocomposites was measured with TG-measurements.

Details

OriginalspracheEnglisch
Seiten (von - bis)3464-3469
Seitenumfang6
FachzeitschriftJournal of nanoscience and nanotechnology
Jahrgang11
Ausgabenummer4
PublikationsstatusVeröffentlicht - 2011
Peer-Review-StatusJa

Externe IDs

PubMed 21776724

Schlagworte

Schlagwörter

  • BiMoO, BiWO, Nanocomposite, Nanoparticles, Poly-laurylacrylate

Bibliotheksschlagworte