The flux growth of InVO₄ bulk single crystals has been explored for the first time. The reported eutectic composition at a ratio of V₂O₅:InVO₄ = 1:1 could not be used as a self-flux since no sign of melting was observed up to 1100 °C. Crystals of InVO₄ of typical size 0.5 × 1 × 7 mm³ were obtained using copper pyrovanadate (Cu₂V₂O₇) as a flux, using Pt crucibles. X-ray powder diffraction confirmed the orthorhombic Cmcm structure. Rests of the flux material were observed on the sample surface, with occasional traces of Pt indicating some level of reaction with the crucible. X-ray absorption spectroscopy showed that oxidation states of indium and vanadium ions are +3 and +5, respectively. The size and high quality of the obtained InVO₄ crystals makes them excellent candidates for further study of their physical properties.